| Výška niklu | Ni+co | Cu | Si | Mn | C | Cr | S | Fe | Mg |
| ≥ | ≤ | ||||||||
| NI201 | Bal. | .25 | .3 | .35 | .02 | .2 | .01 | .3 | - |
| NI200 | Bal. | .25 | .3 | .35 | .15 | .2 | .01 | .3 | - |
| Zliať | Standard Strand Construction, MM | Odpor, Ω/m | Nominálny priemer prameňu, mm | Meter na kilogram |
| NICR 80/20 | 18 × 0,544+1 × 0,574 | 0,252-0,278 | 2.67 | 26 |
| NICR 80/20 | 19 × 0,61 | 0,205-0.250 | 3,05 | |
| NICR 80/20 | 18 × 0,523+1 × 0,574 | 0,271-0,299 | 2.67 | 30 |
| NICR 80/20 | 19 × 0,574 | 0,227-0,251 | 2.87 | 25 |
| NICR 80/20 | 36 x 0,385+1 × 0,45 | 0,265-0,293 | 2.76 | 26 |
| NICR 60/15 | 19 × 0,508 | 0,286-0,318 | 2.54 | |
| NICR 60/15 | 18 × 0,523+1 × 0,574 | 0,276-0.305 | 2.76 | 30 |
| Ni200/ni201 | 19 × 0,574 | 0,019-0.021 | 2.87 | 21 |
| N6 | Chromel C, Ni 60, N6, HAI-NICR 60, TOPHET C, RESISOHM 60, Cronifer II, |
| Electroloy, Nichrome, zliatina C, Ni 6, MWS-675, Stablohm 675 | |
| N7 | Ni 70, Chromel 70/30, N7, Hytemco, Hai-Nicr 70, Balco, Tophet 30, |
| Resisohm 70, Cronix 70, STABLOHM 710 | |
| N8 | Chromel A, Ni 80, N8, Nichrome V, Hai-Nicr 80, Tophet A, ResisoOHM |
| 80, Cronix 80, Protoloy, Ni 8, zliatina A, MWS-650, Stablohm 650 |
| Vlastnosti/známka | CR20NI80 | CR30NI70 | CR15NI60 | CR20NI35 | CR20ni30 | |
| Hlavné chemické zloženie | Ni | Odpočinok | Odpočinok | 55.0-61.0 | 34.0-37.0 | 30.0-34.0 |
| Cr | 20.0-23.0 | 28.0-31.0 | 15.0-18.0 | 18.0-21.0 | 18.0-21.0 | |
| Fe | ≤ 1,0 | ≤ 1,0 | Odpočinok | Odpočinok | Odpočinok | |
| Max. Nepretržitá služba TEMP. prvku | 1200 | 1250 | 1150 | 1100 | 1100 | |
| Odpor pri 20 ° C (μ Ω · m) | 1,09 | 1.18 | 1.12 | 1,04 | 1,04 | |
| Hustota (G/CM3) | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
| Tepelná vodivosť (KJ/M · H · OC) | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
| Koeficient expanzie čiar (a × 10-6/OC) | 18 | 17 | 17 | 19 | 19 | |
| Bod topenia (približne) (OC) | 1400 | 1380 | 1390 | 1390 | 1390 | |
| Predĺženie pri prasknutí (%) | > 20 | > 20 | > 20 | > 20 | > 20 | |
| Mikrografická štruktúra | austenit | austenit | austenit | austenit | austenit | |
| Magnetické vlastnosti | nemagnetický | nemagnetický | nemagnetický | nemagnetický | nemagnetický | |